Thermally enhanced semiconductor package and process for making the same

ABSTRACT

The present disclosure relates to a thermally enhanced semiconductor package, which includes a module substrate, a thinned flip chip die over the module substrate, a mold compound component, a thermally conductive film, and a thermally enhanced mold compound component. The mold compound component resides over the module substrate, surrounds the thinned flip chip die, and extends above an upper surface of the thinned flip chip die to form a cavity over the upper surface of the thinned flip chip die. The thermally conductive film resides over at least the upper surface of the thinned flip chip at the bottom of the cavity. The thermally enhanced mold compound component resides over at least a portion of the thermally conductive film to fill the cavity.

RELATED APPLICATIONS

This application claims the benefit of provisional patent application Ser. No. 62/431,914 filed Dec. 9, 2016 the disclosure of which is hereby incorporated herein by reference in its entirety.

FIELD OF THE DISCLOSURE

The present disclosure relates to a semiconductor package and a process for making the same, and more particularly to a thermally enhanced semiconductor package, and a process to apply a thermally conductive film to the semiconductor package for enhanced thermal performance.

BACKGROUND

With the current popularity of portable communication devices and developed semiconductor fabrication technology, high speed and high performance transistors are more densely integrated on semiconductor dies. Consequently, the amount of heat generated by the semiconductor dies increases significantly due to the large number of transistors integrated on the semiconductor dies, the large amount of power passing through the transistors, and the high operation speed of the transistors. Accordingly, it is desirable to package the semiconductor dies in a configuration for better heat dissipation.

Flip chip assembly technology is widely utilized in semiconductor packaging due to its preferable solder interconnection between flip chip dies and the laminate, on which the flip chip dies are mounted. The flip chip assembly technology eliminates the space needed for wire bonding and the die surface areas of a package, and essentially reduces the overall size of the package. In addition, the elimination of the wire bonding and implementation of a shorter electrical path from the flip chip dies to the laminate reduces undesired inductance and capacitance.

Further, semiconductor dies formed from silicon on insulator (SOI) structures are trending due to the low cost of silicon materials, a large scale capacity of wafer production, well-established semiconductor design tools, and well-established semiconductor manufacturing techniques. However, harmonic generations and low resistivity values of the SOI structures severely limit the SOI's usage in radio-frequency (RF) applications. By using SOI structures in RF fabrications, an interface between the silicon handle layer and an adjacent dielectric layer will generate unwanted harmonic and intermodulation products. Such spectrum degradation causes a number of significant system issues, such as unwanted generation of signals in other RF bands, which the system is attempting to avoid.

To accommodate the increased heat generation of high performance dies and to utilize the advantages of flip chip assembly, it is therefore an object of the present disclosure to provide an improved semiconductor package design with flip chip dies in a configuration for better heat dissipation. In addition, there is also a need to eliminate the deleterious effects of harmonic generations and intermodulation distortions.

SUMMARY

The present disclosure relates to a thermally enhanced semiconductor package, and a process for making the same. According to one embodiment, a thermally enhanced semiconductor package includes a module substrate, a thinned flip chip die over the module substrate, a mold compound component, a thermally conductive film, and a thermally enhanced mold compound component. The thinned flip chip die includes a device layer, a number of interconnects extending from a lower surface of the device layer and coupled to an upper surface of the module substrate, and a dielectric layer over an upper surface of the device layer. The mold compound component resides over the upper surface of the module substrate, surrounds the thinned flip chip die, and extends above an upper surface of the thinned flip chip die to form a cavity over the upper surface of the thinned flip chip die. The thermally conductive film resides over at least the upper surface of the thinned flip chip die at the bottom of the cavity. The thermally enhanced mold compound component resides over at least a portion of the thermally conductive film to fill the cavity.

In one embodiment of the semiconductor package, the thinned flip chip die is formed from a silicon on insulator (SOI) structure. Herein, the device layer of the thinned flip chip die is formed from a silicon epitaxy layer of the SOI structure and the dielectric layer of the thinned flip chip die is a buried oxide layer of the SOI structure.

In one embodiment of the semiconductor package, the thermally conductive film has a higher thermal conductivity than the thermally enhanced mold compound component.

In one embodiment of the semiconductor package, the thermally conductive film has a thermal conductivity between 5 w/m·k and 5000 w/m·k.

In one embodiment of the semiconductor package, the thermally conductive film has a thickness between 0.1 μm to 100 μm.

In one embodiment of the semiconductor package, the thermally conductive film resides over exposed surfaces of the cavity and over the mold compound component to thermally connect the module substrate.

In one embodiment of the semiconductor package, the thermally enhanced mold compound component has a thermal conductivity between 2 w/m·k and 20 w/m·k.

According to an exemplary process, a precursor package including a module substrate, a thinned flip chip die attached to an upper surface of the module substrate, and a mold compound component is provided. Herein, the mold compound component resides over the upper surface of the module substrate, surrounds the thinned flip chip die, and extends above the upper surface of the thinned flip chip die to form a cavity, which is above the upper surface of the thinned flip chip die. Next, a thermally conductive film is deposited over at least the upper surface of the thinned flip chip at the bottom of the cavity. A thermally enhanced mold compound component is then applied over at least a portion of the thermally conductive film to fill the cavity.

Those skilled in the art will appreciate the scope of the present disclosure and realize additional aspects thereof after reading the following detailed description of the preferred embodiments in association with the accompanying drawing figures.

BRIEF DESCRIPTION OF THE DRAWING FIGURES

The accompanying drawing figures incorporated in and forming a part of this specification illustrate several aspects of the disclosure, and together with the description serve to explain the principles of the disclosure.

FIG. 1 shows an exemplary thermally enhanced semiconductor package according to one embodiment of the present disclosure.

FIG. 2 shows an alternative thermally enhanced semiconductor package according to one embodiment of the present disclosure.

FIG. 3 shows an alternative thermally enhanced semiconductor package according to one embodiment of the present disclosure.

FIGS. 4-9 provide exemplary steps that illustrate a process to fabricate the exemplary thermally enhanced semiconductor package shown in FIG. 1.

It will be understood that for clear illustrations, FIGS. 1-9 may not be drawn to scale.

DETAILED DESCRIPTION

The embodiments set forth below represent the necessary information to enable those skilled in the art to practice the embodiments and illustrate the best mode of practicing the embodiments. Upon reading the following description in light of the accompanying drawing figures, those skilled in the art will understand the concepts of the disclosure and will recognize applications of these concepts not particularly addressed herein. It should be understood that these concepts and applications fall within the scope of the disclosure and the accompanying claims.

It will be understood that, although the terms first, second, etc. may be used herein to describe various elements, these elements should not be limited by these terms. These terms are only used to distinguish one element from another. For example, a first element could be termed a second element, and, similarly, a second element could be termed a first element, without departing from the scope of the present disclosure. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items.

It will be understood that when an element such as a layer, region, or substrate is referred to as being “on” or extending “onto” another element, it can be directly on or extend directly onto the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly on” or extending “directly onto” another element, there are no intervening elements present. Likewise, it will be understood that when an element such as a layer, region, or substrate is referred to as being “over” or extending “over” another element, it can be directly over or extend directly over the other element or intervening elements may also be present. In contrast, when an element is referred to as being “directly over” or extending “directly over” another element, there are no intervening elements present. It will also be understood that when an element is referred to as being “connected” or “coupled” to another element, it can be directly connected or coupled to the other element or intervening elements may be present. In contrast, when an element is referred to as being “directly connected” or “directly coupled” to another element, there are no intervening elements present.

Relative terms such as “below” or “above” or “upper” or “lower” or “horizontal” or “vertical” may be used herein to describe a relationship of one element, layer, or region to another element, layer, or region as illustrated in the Figures. It will be understood that these terms and those discussed above are intended to encompass different orientations of the device in addition to the orientation depicted in the Figures.

The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the disclosure. As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. It will be further understood that the terms “comprises,” “comprising,” “includes,” and/or “including” when used herein specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof.

Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. It will be further understood that terms used herein should be interpreted as having a meaning that is consistent with their meaning in the context of this specification and the relevant art and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.

The present disclosure relates to a thermally enhanced semiconductor package, and a process for making the same. FIG. 1 shows an exemplary thermally enhanced semiconductor package 10 according to one embodiment of the present disclosure. For the purpose of this illustration, the exemplary thermally enhanced semiconductor package 10 includes a module substrate 12, two thinned flip chip dies 14, an underfilling layer 16, a mold compound component 18, a thermally conductive film 20, and a thermally enhanced mold compound component 22. In different applications, the thermally enhanced semiconductor package 10 may include fewer or more thinned flip-chip dies.

In detail, the module substrate 12 may be formed from a laminate, a wafer level fan out (WLFO) carrier, a lead frame, a ceramic carrier, or the like. Each thinned flip chip die 14 includes a device layer 24, a number of interconnects 26 extending from a lower surface of the device layer 24 and coupled to an upper surface of the module substrate 12, a dielectric layer 28 over an upper surface of the device layer 24, and essentially no silicon handle layer (not shown) over the dielectric layer 28. Herein, essentially no silicon handle layer over the dielectric layer 28 refers to at most 2 μm silicon handle layer over the dielectric layer 28. In some cases, the thinned flip chip dies 14 do not include any silicon handle layer such that an upper surface of each thinned flip chip die 14 is an upper surface of the dielectric layer 28. The device layer 24 with a thickness between 10 nm and 20000 nm may be formed of silicon oxide, gallium arsenide, gallium nitride, silicon germanium, or the like, and the dielectric layer 28 with a thickness between 10 nm and 20000 nm may be formed of silicon oxide, silicon nitride, or aluminum nitride. The interconnects 26 with a height between 5 μm and 200 μm may be copper pillar bumps, solder ball bumps, or the like.

In one embodiment, each thinned flip chip die 14 may be formed from a silicon on insulator (SOI) structure, which refers to a structure including a silicon handle layer, a silicon epitaxy layer, and a buried oxide layer sandwiched between the silicon handle layer and the silicon epitaxy layer. Herein, the device layer 24 of each thinned flip chip die 14 is formed by integrating electronic components in or on the silicon epitaxy layer of a SOI structure. The dielectric layer 28 of each thinned flip chip die 14 is the buried oxide layer of the SOI structure. In addition, the silicon handle layer of the SOI structure is removed substantially to complete each thinned flip chip die 14 (more details in the following discussion).

The underfilling layer 16 resides over the upper surface of the module substrate 12, such that the underfilling layer 16 encapsulates the interconnects 26 and underfills each thinned flip chip die 14 between the lower surface of the device layer 24 and the upper surface of the module substrate 12. The underfilling layer 16 may be formed from conventional polymeric compounds, which serve to mitigate the stress effects caused by Coefficient of Thermal Expansion (CTE) mismatch between the thinned flip chip dies 14 and the module substrate 12.

The mold compound component 18 resides over the underfilling layer 16, surrounds each thinned flip chip die 14, and extends above the upper surface of each thinned flip chip die 14 to form a cavity 30 over the upper surface of each thinned flip chip die 14. Herein, the upper surface of each thinned flip chip die 14 is exposed at the bottom of the cavity 30. The mold compound component 18 may be formed from a same or different material as the underfilling layer 16. When the mold compound 18 and the underfilling layer 16 are formed from a same material, the mold compound 18 and the underfilling layer 16 may be formed simultaneously. One exemplary material used to form the mold compound component 18 is an organic epoxy resin system.

The thermally conductive film 20 is continuously deposited over exposed surfaces of each cavity 30 and over the mold compound component 18. In some applications, the thermally conductive film 20 may also extend to thermally connect the module substrate 12. Within each cavity 30, the thermally conductive film 20 is immediately above the upper surface of each thinned flip chip die 14 with no significant voids or defects. Herein, no significant voids or defects refers to no voids or defects larger than 0.1 μm between the thermally conductive film 20 and the upper surface of each thinned flip chip die 14. The thermally conductive film 20 has a high thermal conductivity between 5 w/m·k and 5000 w/m·k and a high electrical resistivity greater than 1 E6 Ohm-cm. The thermally conductive film 20 may be formed from chemical vapor deposition (CVD) diamond, aluminum nitride, boron nitride, alumina, beryllium oxide, and the like.

Heat generated by the electronic components in each device layer 24 will travel upward to an area above the upper surface of each thinned flip chip die 14 and then pass laterally in the area above the upper surface of each thinned flip chip die 14 until it is extracted via the interconnects 26 to the module substrate 12. It is therefore highly desirable to have a high thermal conductivity region immediately adjacent to the upper surface of each thinned flip chip die 14 to conduct most of the heat generated by the thinned flip chip dies 14. Consequently, the higher the thermal conductivity in the adjacent region above the upper surface of each thinned flip chip die 14, the better the heat dissipation performance of the thinned flip chip dies 14. Depending on different deposition stresses, different deposited materials, and different applications of the thinned flip chip dies 14, the thermally conductive film 20 has different thicknesses varying from 0.1 μm to 100 μm. For a CVD diamond material, which has an extremely high conductivity greater than 2000 w/m·k, a 1 μm or greater thickness of the thermally conductive film 20 is extremely effective for the heat dissipation management of the thinned flip chip dies 14. For a boron nitride material, which has a high conductivity between 50 w/m·k-100 w/m·k, a 5 μm-10 μm thickness of the thermally conductive film 20 is desirable.

Besides the bottom region of each cavity 30, which is adjacent to the upper surface of each thinned flip chip die 14, the thermally conductive film 20 may also be deposited over the mold compound component 18 and in contact with the module substrate 12. Consequently, the heat generated by the thinned flip chip dies 14 may also dissipate through the thermally conductive film 20 and over the mold compound component 18 to the module substrate 12.

The thermally enhanced mold compound component 22 resides over at least a portion of the thermally conductive film 20 to substantially fill each cavity 30. Although the thermally enhanced mold compound component 22 is not immediately above the thinned flip chip dies 14, the thermally enhanced mold compound component 22 is still close to the thinned flip chip dies 14. Consequently, the thermally enhanced mold compound component 22 is also desired to have a high thermal conductivity and a high electrical resistivity. In this embodiment, the thermally enhanced mold compound component 22 has a lower conductivity than the thermally conductive film 20. The thermally enhanced mold compound component 22 has a thermal conductivity between 2 w/m·k and 20 w/m·k and an electrical resistivity greater than 1 E14 Ohm-cm. One exemplary material used to form the thermally enhanced mold compound component 22 is poly phenyl sulfides (PPS) impregnated with boron nitride additives. In addition, the thermally enhanced mold compound component 22 may be formed from a same or different material as the mold compound component 18. However, unlike the thermally enhanced mold compound component 22, the mold compound 18 does not have a thermal conductivity requirement in higher performing embodiments. In some applications, the thermally enhanced mold compound component 22 may further reside over the mold compound component 18.

It will be clear to those skilled in the art that the thermally conductive film 20 may only be deposited at the bottom region of each cavity 30, which is adjacent to the upper surface of each thinned flip chip die 14. Herein, the thermally conductive film 20 includes two discrete sections as illustrated in FIG. 2, each of which is immediately above the upper surface of a corresponding thinned flip chip die 14. The thermally enhanced mold compound component 22 resides over each section of the thermally conductive film 20 and fills each cavity 30. In this embodiment, the thermally enhanced mold compound component 22 is in contact with the mold compound component 18.

In another embodiment, the thermally enhanced semiconductor package 10 further includes a shielding structure 32 encapsulating the thermally enhanced mold compound component 22 and in contact with the module substrate 12 as illustrated in FIG. 3. Herein, the thermally enhanced mold compound component 22 resides over an entirety of the thermally conductive film 20 so as to provide a planarized surface of the thermally enhanced semiconductor package 10. The shielding structure 32 helps to reduce the electromagnetic interference caused by the thinned flip chip dies 14.

FIGS. 4-9 provide exemplary steps that illustrate a process to fabricate the exemplary thermally enhanced semiconductor package 10 shown in FIG. 1. Although the exemplary steps are illustrated in a series, the exemplary steps are not necessarily order dependent. Some steps may be done in a different order than that presented. Further, processes within the scope of this disclosure may include fewer or more steps than those illustrated in FIGS. 4-9.

Initially, a semiconductor package 34 is provided as depicted in FIG. 4. For the purpose of this illustration, the semiconductor package 34 includes the module substrate 12, two flip chip die 14F, the underfilling layer 16, and the mold compound component 18. In different applications, the semiconductor package 34 may include fewer or more flip chip dies. In detail, each flip chip die 14F includes the device layer 24, the interconnects 26 extending from the lower surface of the device layer 24 and coupled to the upper surface of the module substrate 12, the dielectric layer 28 over the upper surface of the device layer 24, and a silicon handle layer 36 over the dielectric layer 28. As such, the backside of the silicon handle layer 36 is a top surface of each flip chip die 14F.

In one embodiment, each flip chip die 14F may be formed from a SOI structure, which refers to a structure including a silicon handle layer, a silicon epitaxy layer, and a buried oxide layer sandwiched between the silicon handle layer and the silicon epitaxy layer. Herein, the device layer 24 of each flip chip die 14F is formed by integrating electronic components in or on the silicon epitaxy layer of a SOI structure. The dielectric layer 28 of each flip chip die 14F is the buried oxide layer of the SOI structure. The silicon handle layer 36 of each flip chip die 14F is the silicon handle layer of the SOI structure.

In addition, the underfilling layer 16 resides over the upper surface of the module substrate 12, such that the underfilling layer 16 encapsulates the interconnects 24 and underfills each flip chip die 14F between the lower surface of the device layer 22 and the upper surface of the module substrate 12. The mold compound component 18 resides over the underfilling layer 16 and encapsulates the flip chip dies 14F. The mold compound component 18 may be used as an etchant barrier to protect the flip chip dies 14F against etching chemistries such as Tetramethylammonium hydroxide (TMAH), potassium hydroxide (KOH), sodium hydroxide (NaOH), and acetylcholine (ACH) in the following steps.

Next, the mold compound component 18 is thinned down to expose the backside of the silicon handle layer 36 of each flip chip die 14F, as shown in FIG. 5. The thinning procedure may be done with a mechanical grinding process. The following step is to remove substantially the entire silicon handle layer 36 of each flip chip die 14F to create the cavity 30 and provide the thinned flip chip die 14 with the upper surface exposed to the cavity 30, as shown in FIG. 6. Herein, removing substantially the entire silicon handle layer 36 refers to removing at least 95% of the entire silicon handle layer 36, and perhaps a portion of the dielectric layer 28. Because the silicon handle layer 36 is removed substantially, deleterious harmonic generations and intermodulation distortions at an interface between the silicon handle layer 36 and the dielectric layer 28 may be eliminated. Removing substantially the entire silicon handle layer 36 may be provided by an etching process with a wet/dry etchant chemistry, which may be TMAH, KOH, ACH, NaOH, or the like.

The thermally conductive film 20 is then deposited over the exposed surfaces of each cavity 30 and over the mold compound component 18 as illustrated in FIG. 7. The thermally conductive film 20 may also extend to thermally connect the module substrate 12. In each cavity 30, the thermally conductive film 20 is immediately above the upper surface of each thinned flip chip die 14 with no significant voids or defects. Depositing the thermally conductive film 20 may be provided by Chemical Vapor Deposition (CVD) or Atomic Layer Deposition (ALD) with a temperature between 150° C. and 300° C. According to different depositing processes with different materials, a protecting procedure to a lower surface of the module substrate 12, which contains the electrical input/output contact regions, may be applied before the deposition (not shown).

After the thermally conductive film 20 is deposited over the exposed surfaces of each cavity 30 and over the mold compound component 18, a thermally enhanced mold compound 22M is applied over at least a portion of the thermally conductive film 20 to substantially fill each cavity 30 as depicted in FIG. 8. Notice that the thermally enhanced mold compound 22M does not directly reside over the upper surface of the thinned flip chip dies 14. In some cases, the thermally enhanced mold compound 22M may further reside over the mold compound component 18. A curing process (not shown) is followed to harden the thermally enhanced mold compound 22M in order to form the thermally enhanced mold compound component 22. The curing temperature is between 100° C. and 320° C. depending on which material is used as the thermally enhanced mold compound 22M. Normally, the thermally conductive film 20 has a higher thermal conductivity than the thermally enhanced mold compound component 22, such that the bottom region of each cavity 30 (adjacent to the upper surface of each thinned flip chip die 14) has better heat dissipation performance than the rest of the cavity 30.

An upper surface of the thermally enhanced mold compound component 22 is then planarized to form the thermally enhanced semiconductor package 10 as depicted in FIG. 9. A mechanical grinding process may be used for planarization. The thermally enhanced mold compound component 20 may reside over the mold compound component 18. Finally, the thermally enhanced semiconductor package 10 may be marked, diced, and singulated into individual components.

Those skilled in the art will recognize improvements and modifications to the preferred embodiments of the present disclosure. All such improvements and modifications are considered within the scope of the concepts disclosed herein and the claims that follow. 

1. An apparatus comprising: a module substrate having an upper surface; a thinned flip chip die comprising: a device layer comprising electronic components; a dielectric layer over an upper surface of the device layer; and a plurality of interconnects extending from a lower surface of the device layer and coupled to the upper surface of the module substrate; a mold compound component residing over the upper surface of the module substrate, surrounding the thinned flip chip die, and extending above an upper surface of the thinned flip chip die to form a cavity over the upper surface of the thinned flip chip die, wherein the mold compound component is not over the thinned flip chip die; a thermally conductive film residing over at least the upper surface of the thinned flip chip die at a bottom of the cavity; and a thermally enhanced mold compound component residing over at least a portion of the thermally conductive film to fill the cavity.
 2. The apparatus of claim 1, wherein the thinned flip chip die is formed from a silicon on insulator (SOI) structure, wherein the device layer of the thinned flip chip die is formed from a silicon epitaxy layer of the SOI structure, and the dielectric layer of the thinned flip chip die is a buried oxide layer of the SOI structure.
 3. The apparatus of claim 1 wherein the thermally conductive film has a higher thermal conductivity than the thermally enhanced mold compound component.
 4. The apparatus of claim 1 wherein the thermally conductive film has a thermal conductivity between 5 w/m·k and 5000 w/m·k.
 5. The apparatus of claim 1 wherein the thermally conductive film has a thickness between 0.1 μm to 100 μm.
 6. The apparatus of claim 1 wherein the thermally conductive film is formed from chemical vapor deposition (CVD) diamond.
 7. The apparatus of claim 6 wherein the thermally conductive film has a thickness greater than 1 μm.
 8. The apparatus of claim 1 wherein the thermally conductive film is formed from boron nitride.
 9. The apparatus of claim 8 wherein the thermally conductive film has a thickness between 5 μm and 10 μm.
 10. The apparatus of claim 1 wherein the thermally conductive film is formed from one of a group consisting of aluminum nitride, alumina, and beryllium oxide.
 11. The apparatus of claim 1 wherein the thermally enhanced mold compound component has a thermal conductivity between 2 w/m·k and 20 w/m·k.
 12. The apparatus of claim 1 wherein the thermally conductive film resides over exposed surfaces of the cavity and over the mold compound component to thermally connect the module substrate.
 13. The apparatus of claim 1 wherein the thermally enhanced mold compound component resides over an entirety of the thermally conductive film.
 14. The apparatus of claim 13 further comprises a shielding structure that encapsulates the thermally enhanced mold compound component and is in contact with the module substrate.
 15. The apparatus of claim 1 further comprising an underfilling layer residing between the mold compound component and the upper surface of the module substrate, and underfilling the thinned flip chip die between the lower surface of the device layer and the upper surface of the module substrate.
 16. The apparatus of claim 15 wherein the underfilling layer is formed from a same material as the mold compound component.
 17. A method comprising: providing a precursor package including a module substrate, a thinned flip chip die attached to an upper surface of the module substrate, and a mold compound component, wherein the mold compound component resides over the upper surface of the module substrate, surrounds the thinned flip chip die, and extends above an upper surface of the thinned flip chip die to form a cavity, which is above the upper surface of the thinned flip chip die; depositing a thermally conductive film over at least the upper surface of the thinned flip chip die at a bottom of the cavity; and applying a thermally enhanced mold compound component over at least a portion of the thermally conductive film to fill the cavity.
 18. The method of claim 17 further comprising a protecting procedure to a lower surface of the module substrate before depositing the thermally conductive film.
 19. The method of claim 17 wherein depositing the thermally conductive film is provided by Chemical Vapor Deposition (CVD) or Atomic Layer Deposition (ALD).
 20. The method of claim 17 wherein providing the precursor package comprises: providing a semiconductor package including the module substrate, a flip chip die attached to the upper surface of the module substrate, and the mold compound component over and surrounding the flip chip die; thinning the mold compound component down to expose a backside of a silicon handle layer of the flip chip die; and removing substantially the entire silicon handle layer to form the cavity and provide the thinned flip chip die with the upper surface, wherein the upper surface of the thinned flip chip die is exposed to the cavity.
 21. The method of claim 20 wherein the flip chip die is formed from a SOI structure and comprises: a device layer; a dielectric layer over an upper surface of the device layer; and a plurality of interconnects extending from a lower surface of the device layer and coupled to the upper surface of the module substrate, wherein the device layer of the flip chip die is formed from a silicon epitaxy layer of the SOI structure, the dielectric layer of the flip chip die is a buried oxide layer of the SOI structure, and the silicon handler layer of the flip chip die is a silicon handle layer of the SOI structure. 